SpecChem > Products > SpecPoxy 2000 LPL

SpecPoxy 2000 LPL Green Conscious Product

ASTM 881 compliant hi-mod, LPL, medium viscosity epoxy

SpecPoxy 2000 LPL is a two-component, long pot life, multi-purpose, high-modulus, moisture-tolerant epoxy bonding adhesive. This medium-viscosity, solvent-free bonder is designed for a variety of structural bonding applications and meets the requirements of ASTM C881, Types I, II, IV, & V, grade 2, classes B&C.

  • Long open time allows for extended workability.
  • Can be used for bonding overlays.
  • Suitable for both fresh and hardened concrete.
  • Effective for gravity filling of concrete cracks.
Tech Sheet
Safety Sheet
Spanish Tech Sheet

Application

  • Bonds fresh concrete to hardened concrete.
  • Anchors steel to fresh concrete.
  • Used for gravity filling cracks in concrete.
  • VOC content is 0 grams per liter, emphasizing its environmental safety.

Mixing Instructions

  • Premix each component separately, then mix two parts of Part A with one part of Part B for three minutes using a low-speed drill.
  • Ensure all materials are at least 40°F prior to mixing and installation.

Surface Preparation

  • Surfaces must be clean and structurally sound, free from oil, grease, dirt, and other contaminants.
  • Recommended methods include abrasive blast cleaning and mechanical removal.
  • Ensure drilled holes are cleaned out with a cylindrical bristle brush and oil-free compressed air.

Application Techniques

  • Bonding: Apply at a rate of 80 sq ft per gallon, approximately 20 mils in thickness.
  • Patching: To create a mortar, mix one part SpecPoxy 2000 LPL with one to four parts clean, dry silica sand. First, apply a prime coat of the neat mixed epoxy before the mortar.

Packaging

  • Available in 1 gallon units, 3 gallon units, and 15 gallon units.

Shelf Life

  • Store in original, tightly closed containers in a clean, dry area. Properly stored, the shelf life is two years from the date of manufacture.

Test Data

  • ASTM Compliance: ASTM C881 compliant for high-modulus, medium-viscosity applications.
  • Initial Cure: 24 hours
  • Final Cure: 7 days
  • Compressive Strength (ASTM D695): 10,150 psi
  • Compressive Modulus (ASTM D695): 186,500 psi
  • Bond Strength (ASTM 882): 2 days – 1,850 psi; 14 days – 2,350 psi
  • Elongation (ASTM D638): 2.1%
  • Tensile Strength (ASTM D638): 4,350 psi
  • Water Absorption (ASTM D570): <0.5%
  • Mix Ratio: 2 to 1

Standards

  • ASTM Compliance: ASTM C881 compliant for high-modulus, medium-viscosity applications.